A 2000-year perspective on indentation crack resistance and brittleness of glass

Year:

2015

Type of Publication:

Artikel

Schlüsselwörter:

Archeological glasses

Autoren:

Hasdemir, Ilhan; Striepe, Simon; Deubener, Joachim; Simon, Klaus

Journal:

Journal of Non-Crystalline Solids

Volume:

408

Seiten:

51 - 56

ISSN:

0022-3093

BibTex:

@article{Hasdemir201551, author = "Ilhan Hasdemir and Simon Striepe and Joachim Deubener and Klaus Simon", abstract = "Abstract Data on micromechanical properties of ancient and medieval glass fragments and glasses of early modern and today{\&}#039;s manufacturing were compiled to offer a tentative look on changes in the brittleness of glass over the past 2000 years. Chronology of glass making was based on glass chemistry using rare earth element (REE) pattern, fluxing agents and provenance analysis while cracking and brittleness were evaluated from Vickers indentation in the course of the mean crack initiation load \{CR\} and the crack length-to-half diagonal ratio c/a. A structural analysis revealed that \{CR\} increases and c/a decreases with increasing molar volume i.e. decreasing atomic packing fraction, which allows us to classify periods of high and low crack-resistant and brittle glasses along the time line of historic glass technology. ", doi = "http://dx.doi.org/10.1016/j.jnoncrysol.2014.10.012", issn = "0022-3093", journal = "Journal of Non-Crystalline Solids ", keywords = "Archeological glasses", pages = "51 - 56", title = "{A} 2000-year perspective on indentation crack resistance and brittleness of glass ", url = "http://www.sciencedirect.com/science/article/pii/S0022309314005225", volume = "408", year = "2015", }

Kurzzusammenfassung:

Abstract Data on micromechanical properties of ancient and medieval glass fragments and glasses of early modern and today's manufacturing were compiled to offer a tentative look on changes in the brittleness of glass over the past 2000 years. Chronology of glass making was based on glass chemistry using rare earth element (REE) pattern, fluxing agents and provenance analysis while cracking and brittleness were evaluated from Vickers indentation in the course of the mean crack initiation load \{CR\} and the crack length-to-half diagonal ratio c/a. A structural analysis revealed that \{CR\} increases and c/a decreases with increasing molar volume i.e. decreasing atomic packing fraction, which allows us to classify periods of high and low crack-resistant and brittle glasses along the time line of historic glass technology.